Frit Slurry migrating from COE96 world

For discussion of processes related to using Bullseye glass, including kilnforming and kilncasting, torchwork, blowing and stained glass.

Frit Slurry migrating from COE96 world

Postby tsuhler » Wed Mar 14, 2018 8:26 am

I have created pieces with a frit slurry using a fuse and slump in one firing with system 96 glass.
I would like to now start using Bullseye coe90 glass and have some questions.

I begin by creating a design with frit slurry on 5mm clear sheet glass. The piece is then placed on a slump mold. Bullseye does not have 5mm glass.

1) Do you recommend using 4mm or 6mm glass?
2) Should I be using the clear Tekta for the sheet glass?
3) Firing schedule. The firing schedule below is what I have been using. Would you suggest making any changes to this schedule?

Fuse and Slump in One Firing
Segment Rate Temp in F Hold in mins
1 200 190 30
2 200 550 10
3 275 1215 45
4 350 1400 03
5 9000 950 60
6 100 500 0
tsuhler
 
Posts: 1
Joined: Wed Mar 14, 2018 8:13 am

Re: Frit Slurry migrating from COE96 world

Postby jestersbaubles » Sat Mar 17, 2018 6:59 am

Are you sure you were using 5 mm glass? System 96 is typically the standard 3 mm and 6 mm. IMO, 1 mm wouldn't make much difference in how you approach a fairly inexact technique like frit slurries anyway (how do you precisely dial in the amount of slurry you're actually applying to the glass? You don't!).

Bullseye has a wealth of information about their firing schedules. You should be able to find recommended temperatures for full-fuse, slumping, annealing, etc. A great place to start is here: https://www.bullseyeglass.com/what-temp ... using.html

Once you've had a chance to experiment on your own, come back with questions you may have regarding the results!

Best, Dana
Dana Worley Fused Glass Designs
dba Jester's Baubles
http://www.jestersbaubles.com
http://www.jestersbaubles.blogspot.com
jestersbaubles
 
Posts: 232
Joined: Thu Jan 21, 2010 6:29 pm
Location: Logan, UT

Re: Frit Slurry migrating from COE96 world

Postby marykaynitchie » Fri Mar 23, 2018 9:47 am

I think that 4mm Tekta would be fine for this, so I would try that first, and then 6mm Tekta if it doesn't.

Mary Kay
Mary Kay Nitchie
Bullseye Glass Co.

Subscribe to Bullseye kiln-glass videos at