I have created pieces with a frit slurry using a fuse and slump in one firing with system 96 glass.
I would like to now start using Bullseye coe90 glass and have some questions.
I begin by creating a design with frit slurry on 5mm clear sheet glass. The piece is then placed on a slump mold. Bullseye does not have 5mm glass.
1) Do you recommend using 4mm or 6mm glass?
2) Should I be using the clear Tekta for the sheet glass?
3) Firing schedule. The firing schedule below is what I have been using. Would you suggest making any changes to this schedule?
Fuse and Slump in One Firing
Segment Rate Temp in F Hold in mins
1 200 190 30
2 200 550 10
3 275 1215 45
4 350 1400 03
5 9000 950 60
6 100 500 0