Hi everyone. I have a question and would like feedback.I have a kiln that fires "cold" so if I program for 1000 it's like the temperature only gets to 975, so I adjust the firing schedule accordingly.
I have not done a cone test. So if I was to anneal bullseye at a set temp in my "cold kiln" @ 925 degrees (wanting 900 degrees as the anneal temp) and if I am wrong about the temperatures (that 25 degrees) do you think the piece will anneal sufficiently? Since they adjust the annealing temps some time back, does annealing in the range between 900 to 960 still provide a stable anneal??