Your help please!
I need some advise on an idea I have had.
Side A: 3mm clear #1100 sheet glass used as a base.
Apply let us say six(6) layers of any powder of your choice. Then a roughly the same amount of clear #1101 powder as a cap.
Fire to full fuse.
The question I have is can you now apply powder to the other side of the aforementioned piece?
If so how much powder and to what firing schedule would you use. Also what affect would this have on side A?
Your help in this matter is deeply appreciated.