I started over and did a new piece the glass had a few pieces here and there of flaws, I took and used the glass any way, put it through the fusing, just looked at it there is a crack AGAIN.
Does anyone know if I run it through the fusing stage again if the crack will fuse or will it just
make it worse? One would think if you can take a broken piece and butt it up against the area it
came off, fusing back together you be able to get the crack to fuse together. That is just my thinking. Should I give it a try or am I wasting my time.